APM FeCrAl Heating Strip with 1400°C Max Temperature for Industrial Furnace Heating via Powder Metallurgy

Détails de produit

Conditions de paiement et d'expédition

Quantité de commande min: 50 kg

Prix: Négociable

Détails d'emballage: Emballage carton + boîte en bois

Délai de livraison: 10-30 jours

Conditions de paiement: T/T

Capacité d'approvisionnement: 500 tonnes par mois

Obtenez le meilleur prix

Contactez-nous maintenant

Les spécifications

Définition

Les spécifications

Mettre en évidence: 
                                                                                                                                                                                                                                                                                                                                                                                                                                                                                                                                                                                                                                                                                                                              APM FeCrAl heating strip, high temperature resistance heating strip, Copper Nickel alloy heating wire
                                                  

Matériel:	Alliage fédéral	Grade:	APM
Forme:	Bande	Épaisseur:	0,08-2,80 mm
Largeur:	10-200 millimètres	Surface:	Brillant / Oxydé
Condition:	Doux	Résistivité:	1,53 Ω·mm²/m
Température de fonctionnement maximale:	1400°C	Processus de production:	Métallurgie des poudres
Application:	Chauffage de four industriel	MOQ:	Négociable

Matériel:	Alliage fédéral
Grade:	APM
Forme:	Bande
Épaisseur:	0,08-2,80 mm
Largeur:	10-200 millimètres
Surface:	Brillant / Oxydé
Condition:	Doux
Résistivité:	1,53 Ω·mm²/m
Température de fonctionnement maximale:	1400°C
Processus de production:	Métallurgie des poudres
Application:	Chauffage de four industriel
MOQ:	Négociable

Définition

APM FeCrAl Heating Strip with 1400°C Max Temperature for Industrial Furnace Heating via Powder Metallurgy

Powder Metallurgy APM FeCrAl Heating Alloy Wire up to 1400°C

This product takes refined master alloy as raw material, uses powder metallurgy technology to manufacture alloy ingots, and is manufactured by special cold and hot processing and heat treatment process. The product has the advantages of strong oxidation resistance, good corrosion resistance at high temperature, small creep of electrothermal components, long service life at high temperature and small change of resistance. It is suitable for high temperature 1400 C, high power density, corrosive atmosphere, carbon atmosphere and other working environments. It can be used in ceramic kilns, high temperature heat treatment furnaces, laboratory furnaces,
electronic industrial furnaces and diffusion furnaces.

Main composition

	C	Si	Mn	Cr	Al	Fe
Min	-	-	-	20	5.5	Bal.
Max	0.04	0.5	0.4	22	6.0	Bal.

Main mechanical properties
Tensile Strength at Room Temperature: 650-750MPa
Elongation rate: 15-25%
Hardness: HV220-260
1000ºC Tensile Strength at 1000ºC Temperature 22-27MPa
1000ºC 6MPa High Temperature Durability at 1000 Temperature and 6MPa ≥100h
Main physical properties

Density 7.1g/cm3
Resistivity 1.53×10-6 Ω.m
Resistance Temperature Coefficient(Ct)
Melting point:1500ºC
Maximum Continuous Working Temperature 1400ºC

800ºC	1000ºC	1400ºC
1.03	1.04	1.05

Average linear expansion coefficient

20-800ºC	20-1000ºC	20-1400ºC
14	15	16

Fast life

	1400ºC	1370ºC
Average Fast Life (Hours)	178	>500
Sagging rate after rupture	8	11

1400°C APM Heating Strip for Glass Industry Furnaces Factory price

Tags:

Veuillez nous envoyer votre demande et nous te répondrons dès que possible.

Envoyez

Fil en alliage de cuivre Nickel

Fil de résistance électrique

Fil nu de thermocouple

Alliage de Fecral

Câble de thermocouple

Alliage de Nicr

Fil thermique de jet

Élément de chauffe de four

Alliage de précision

Alliage de cuivre

Alliage de nickel

Fil émaux

Alliage à hautes températures

Prise de thermocouple

APM FeCrAl Heating Strip with 1400°C Max Temperature for Industrial Furnace Heating via Powder Metallurgy